I'm taking my aluminum parts to be anodized.
Are there any parts that should not be anodized?
I have the option of Type II or Type III Hard Coat. Thoughts?
Thanks,
Joe
I would be careful anodizing the spindles where they need to slip fit inside the bearings and also you will need to chase all the threads. There are a couple other posts in here where builders have anodized their parts where you might see more feedback.